性能項目 |
試驗條件[狀態(tài)] |
測試方法 |
測試數據 |
數據單位 |
|
物理性能 |
比重 |
|
ASTM D-792 |
1.62 |
|
|
模具收縮率 |
1.6mm(0.063in) |
ASTM D-955 |
-0.1 |
% |
|
機械性能 |
彎曲模量 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-790 |
14000 |
MPa |
|
IZOD沖擊強度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-256 |
225 |
J/m |
|
拉伸強度 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
173 |
MPa |
|
拉伸模量 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
19306 |
MPa |
|
IZOD沖擊強度 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-256 |
170 |
J/m |
|
拉伸強度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
150 |
MPa |
|
彎曲強度 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
215 |
MPa |
|
無(wú)缺口沖擊強度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-4812 |
740，20%NB |
J/m |
|
彎曲模量 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-790 |
18000 |
MPa |
|
彎曲強度 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
183 |
MPa |
|
壓縮強度 |
3.2mm(0.125in) |
ASTM D-695 |
89 |
MPa |
|
斷裂伸長(cháng)率 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-638 |
1.6 |
% |
|
彎曲模量 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-790 |
13100 |
MPa |
|
IZOD沖擊強度 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-256 |
400,40%NB |
J/m |
|
剪切強度 |
0.8mm(0.032in) |
ASTM D-732 |
57 |
MPa |
|
彎曲強度 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-790 |
192 |
MPa |
|
斷裂伸長(cháng)率 |
3.2mm(0.125in) |
ASTM D-638 |
1.7 |
% |
|
無(wú)缺口沖擊強度 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-4812 |
840 |
J/m |
|
洛氏硬度 |
|
ASTM D-785 |
63 |
|
|
拉伸模量 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-638 |
18000 |
MPa |
|
壓縮模量 |
3.2mm(0.125in) |
ASTM D-695 |
5300 |
MPa |
|
剪切強度 |
3.2mm(0.125in) |
ASTM D-732 |
58 |
MPa |
|
無(wú)缺口沖擊強度 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-4812 |
NB |
J/m |
|
電氣性能 |
損耗因數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
0.004 |
|
|
介電常數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-2520 B |
4.3 |
|
|
損耗因數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-150 |
0.029 |
|
|
介電常數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-150 |
3.8 |
|
|
介電常數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-150 |
3.5 |
|
|
介電常數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
4.4 |
|
|
損耗因數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-150 |
0.013 |
|
|
損耗因數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-150 |
0.029 |
|
|
介電常數 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
4.3 |
|
|
表面電阻率 |
|
ASTM D-257 |
1×1015 |
Ohm |
|
介電常數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-150 |
3.9 |
|
|
介電常數 |
3.2mm(0.125in),23℃(73℉) |
ASTM D-150 |
4.3 |
|
|
體積電阻率 |
|
ASTM D-257 |
1×1016 |
Ohm-cm |
|
介電強度 |
3.2mm,23℃(73℉) |
ASTM D-149 |
>28 |
Kv/mm |
|
損耗因數 |
1.6mm(0.063in),23℃(73℉) |
ASTM D-2520 B |
0.004 |
|
|
介電強度 |
1.6mm,23℃(73℉) |
ASTM D-149 |
35 |
Kv/mm |
|
損耗因數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-150 |
0.013 |
|
|
損耗因數 |
0.8mm(0.032in),23℃(73℉) |
ASTM D-2520 B |
0.004 |
|
|
介電強度 |
1.6mm(0.063in) |
ASTM D-149 |
31 |
Kv/mm |
|
熱性能 |
表面電阻率 |
|
ASTM D-257 |
1×1015 |
Ohm |
|
熔點(diǎn) |
|
ASTM D-3418 |
352 |
℃ |
|
解鏈溫度范圍 |
|
|
363-371 |
℃ |
|
熱導率 |
|
ASTM C-177 |
0.32 |
W/mk |
|
模壓溫度范圍 |
|
|
30-95 |
℃ |
|
玻璃化轉變溫度 |
|
ASTM D-3418 |
120 |
℃ |
|
干燥溫度 |
|
|
135 |
℃ |
|
熱變形溫度 |
1.80MPa |
ASTM D-648 |
289 |
℃ |
|
其它性能 |
RTI,Mechanical with Impact |
1.5mm |
UL 746-B |
210 |
℃ |
|
RTI,Electrical |
3.0mm |
UL 746-B |
240 |
℃ |
|
RTI,Mechanical without Impact |
1.5mm |
UL 746-B |
240 |
℃ |
|
RTI,Electrical |
0.75mm |
UL 746-B |
240 |
℃ |
|
RTI,Mechanical without Impact |
0.75mm |
UL 746-B |
240 |
℃ |
|
RTI,Mechanical with Impact |
3.0mm |
UL 746-B |
210 |
℃ |
|
RTI,Mechanical without Impact |
3.0mm |
UL 746-B |
240 |
℃ |
|
RTI,Electrical |
1.5mm |
UL 746-B |
240 |
℃ |